Part 4 - unalloyed and low alloyed steels "weatherproof" and "alloyed"
Quality |
Standard |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
V |
Re |
Rm |
A |
KV |
at |
|
|
Cu |
Al |
Ti+Zr |
|
|
|
|
|
|
MPa |
MPa |
(%) |
(J) |
°C |
Wire electrodes for arc welding GMAW |
|||||||||||||||
DR-SG 2
|
EN ISO 14341-A: G3Si1 |
0,06-0,14 |
0,70-1,00 |
1,30-1,60 |
0,025 |
0,025 |
0,150 |
0,150 |
0,150 |
0,030 |
>420 |
>520 |
>
27 |
>100 |
20 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Material-No.: 1.5125 |
0,350 |
0,020 |
0,150 |
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.18: ER 70 S-6 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 3
|
EN ISO 14341-A: G4Si1 |
0,06-0,14 |
0,70-1,00 |
1,30-1,60 |
0,025 |
0,025 |
0,150 |
0,150 |
0,150 |
0,030 |
>460 |
>560 |
>
27 |
>
47 |
20 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Material-No.: 1.5130 |
0,350 |
0,020 |
0,150 |
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.18: ER 70 S-6 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG NiCu
|
EN ISO 14341-A: G3Ni1 |
0,06-0,14 |
0,50-0,90 |
1,00-1,60 |
0,020 |
0,020 |
0,80-1,50 |
0,150 |
0,150 |
0,030 |
>450 |
>550 |
>
16 |
>
80 |
20 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,350 |
0,020 |
0,150 |
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 80 S-Ni1 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG Ni 2,5
|
EN ISO 14341-A: G2Ni2 |
0,06-0,14 |
0,40-0,80 |
0,80-1,40 |
0,020 |
0,020 |
2,10-2,70 |
0,150 |
0,150 |
0,030 |
>510 |
>610 |
>
22 |
>
47 |
- 80 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,350 |
0,020 |
0,150 |
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 80 S-Ni2 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 2 Ni
|
EN ISO 14341-A: G3Ni1 |
0,06-0,14 |
0,50-0,90 |
1,00-1,60 |
0,020 |
0,020 |
0,80-1,50 |
0,150 |
0,150 |
0,030 |
>490 |
>600 |
>
16 |
>
80 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,350 |
0,020 |
0,150 |
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 80 S-Ni1 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Flux cored wires for arc welding GMAW |
|||||||||||||||
DR-F MPR 01
|
EN ISO 17632-A: T46 4 M M 2 H5 / T42
4 M C 2 H5 |
|
|
2,000 |
|
|
0,500 |
0,200 |
0,200 |
0,080 |
>460 |
>530 |
>
22 |
>
47 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.18: E70C-6MH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F RPR 01
|
EN ISO 17632-A: T46 2 P M 1 H5 / T42
2 P C 1 H5 |
|
|
2,000 |
|
|
0,500 |
0,200 |
0,200 |
0,080 |
>460 |
>530 |
>
22 |
>
47 |
-20 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E71T1-(M)H4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F BPR 01
|
EN ISO 17632-A: T46 4 B M 4 H5 / T42
4 B C 4 H5 |
|
|
2,000 |
|
|
0,500 |
0,200 |
0,200 |
0,080 |
>460 |
>550 |
>
22 |
>
47 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E70T5-(M)H4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F MPR 10
|
EN ISO 17632-A: T46 6 1Ni M M 2 H5 |
|
0,800 |
1,400 |
|
|
0,60-1,20 |
0,200 |
0,200 |
0,080 |
>460 |
>530 |
>
20 |
>
47 |
-60 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
2,000 |
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E80C-Ni1MH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F RPR 10
|
EN ISO 17632-A: T50 6 1Ni P M 1 H5 |
|
0,800 |
1,400 |
|
|
0,60-1,20 |
0,200 |
0,200 |
0,080 |
>500 |
>560 |
>
18 |
>
47 |
-60 °C |
|
EN ISO 17632-A: T46 5 1Ni P C 1 H5 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
2,000 |
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E81T1-Ni1(M)JH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Quality |
Standard |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
V |
Re |
Rm |
A |
KV |
at |
|
|
Cu |
Al |
Ti+Zr |
|
|
|
|
|
|
MPa |
MPa |
(%) |
(J) |
°C |
Flux cored wires for arc welding GMAW |
|||||||||||||||
DR-F BPR 10
|
EN ISO 17632-A: T46 6 1Ni B M 3 H5 |
|
0,800 |
1,400 |
|
|
0,60-1,20 |
0,200 |
0,200 |
0,080 |
>500 |
>560 |
>
18 |
>
47 |
-60 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
2,000 |
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E80T5-NiMH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F MPR 13
|
EN ISO 17632-A: T46 6 2Ni M M 2 H5 |
|
|
1,400 |
|
|
1,80-2,60 |
0,200 |
0,200 |
0,080 |
>460 |
>530 |
>
20 |
>
47 |
-60 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
2,000 |
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E80C-Ni2MH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F RPR 13
|
EN ISO 17632-A: T46 6 2Ni P M 1 H5 |
|
|
1,400 |
|
|
1,80-2,60 |
0,200 |
0,200 |
0,080 |
>460 |
>530 |
>
20 |
>
47 |
-60 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
2,000 |
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E81T1-Ni2MJH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F BPR 13
|
EN ISO 17632-A: T50 6 2Ni B M 3 H5 |
|
|
1,400 |
|
|
1,80-2,60 |
0,200 |
0,200 |
0,080 |
>500 |
>560 |
>
18 |
>
47 |
-60 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
2,000 |
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E80T5-Ni2MH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F MPR 30
|
EN ISO 17632-A: T46 4 Z M M 2 H5 |
0,060 |
0,450 |
1,200 |
0,025 |
0,025 |
0,500 |
|
|
|
>460 |
>530 |
>
20 |
>
47 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,500 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E80C-GMH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F RPR 30
|
EN ISO 17632-A: T46 2 Z P M 1 H5 |
0,050 |
0,400 |
1,200 |
0,025 |
0,025 |
1,200 |
|
|
|
>460 |
>530 |
>
20 |
>
47 |
-20 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,400 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E81T1-WGMH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F BPR 30
|
EN ISO 17632-A: T42 4 Z B M 3 H5 |
0,050 |
0,450 |
1,200 |
0,025 |
0,025 |
1,200 |
|
|
|
>420 |
>500 |
>
20 |
>
47 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,500 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E70T5-WGMH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Welding rods for arc welding TIG |
|||||||||||||||
DR-SG 2
|
EN ISO 636-A: W3Si1 |
0,06-0,14 |
0,70-1,00 |
1,30-1,60 |
0,025 |
0,025 |
0,150 |
0,150 |
0,150 |
0,030 |
>420 |
>520 |
>
27 |
>100 |
20 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Material-No.: 1.5125 |
|
0,030 |
0,150 |
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.18: ER 70 S-6 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 3
|
EN ISO 636-A: W4Si1 |
0,06-0,14 |
0,70-1,00 |
1,60-1,90 |
0,025 |
0,025 |
0,150 |
0,150 |
0,150 |
0,030 |
>460 |
>560 |
>
27 |
>
47 |
20 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Material-No.: 1.5130 |
|
0,020 |
0,150 |
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.18: ER 70 S-6 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Quality |
Standard |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
V |
Re |
Rm |
A |
KV |
at |
|
|
Cu |
Al |
Ti+Zr |
|
|
|
|
|
|
MPa |
MPa |
(%) |
(J) |
°C |
Welding rods for arc welding TIG |
|||||||||||||||
DR-SG NiCu
|
EN ISO 636-A: W3Ni1 |
0,06-0,14 |
0,50-0,90 |
1,00-1,60 |
0,020 |
0,020 |
0,80-1,50 |
0,150 |
0,150 |
0,030 |
>450 |
>550 |
>
16 |
>
80 |
20 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,350 |
0,020 |
0,150 |
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 80 S-Ni1 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG Ni 2,5
|
EN ISO 636-A: W2Ni2 |
0,06-0,14 |
0,40-0,80 |
0,80-1,40 |
0,020 |
0,020 |
2,10-2,70 |
0,150 |
0,150 |
0,030 |
>510
|
>610 |
> 22 |
> 47 |
-80 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,020 |
0,150 |
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 80 S-Ni2 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 2 Ni
|
EN ISO 636-A: W3Ni1 |
0,06-0,14 |
0,50-0,90 |
1,00-1,60 |
0,020 |
0,020 |
0,80-1,50 |
0,150 |
0,150 |
0,030 |
>490
|
>600 |
> 25 |
>100 |
20 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,020 |
0,150 |
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 80 S-Ni1 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Quality |
Standard |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
V |
Re |
Rm |
A |
KV |
at |
|
|
Cu |
Al |
Ti+Zr |
|
|
|
|
|
|
MPa |
MPa |
(%) |
(J) |
°C |
Wire electrodes for submerged arc welding SAW |
|||||||||||||||
DR-S NiCu
|
EN ISO 14171-A: S2Ni1Cu |
0,08-0,12 |
0,15-0,35 |
0,70-1,20 |
0,020 |
0,020 |
0,65-0,90 |
0,400 |
0,150 |
|
The mechanical properties are largely determined by the applied
fluxes.
|
||||
|
|
|
|
|
|
|
|
|
|
|
|||||
|
|
0,40-0,65 |
0,030 |
|
|
|
|
|
|
|
|||||
|
AWS/ASME-A5.23: EG |
|
|
|
|
|
|
|
|
|
|||||
DR-S 2 Ni 1
|
EN ISO 14171-A: S2Ni1 |
0,07-0,15 |
0,05-0,25 |
0,80-1,30 |
0,020 |
0,020 |
0,80-1,20 |
0,150 |
0,150 |
|
The mechanical properties are largely determined by the applied
fluxes.
|
||||
|
|
|
|
|
|
|
|
|
|
|
|||||
|
Material-No.: 1.6225 |
0,300 |
0,030 |
|
|
|
|
|
|
|
|||||
|
AWS/ASME-A5.23: E Ni 1 |
|
|
|
|
|
|
|
|
|
|||||
DR-S 2 Ni 2
|
EN ISO 14171-A: S2Ni2 |
0,07-0,15 |
0,05-0,25 |
0,80-1,30 |
0,020 |
0,020 |
1,80-2,40 |
0,150 |
0,150 |
|
The mechanical properties are largely determined by the applied
fluxes.
|
||||
|
|
|
|
|
|
|
|
|
|
|
|||||
|
Material-No.: 1.6227 |
0,300 |
0,030 |
|
|
|
|
|
|
|
|||||
|
AWS/ASME-A5.23: E Ni 2 |
|
|
|
|
|
|
|
|
|
Quality |
Standard |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
V |
Re |
Rm |
A |
KV |
at |
|
|
Cu |
Al |
Ti+Zr |
|
|
|
|
|
|
MPa |
MPa |
(%) |
(J) |
°C |
Flux cored wire for submerged arc welding |
|||||||||||||||
DR-FS MPR 01
|
DIN EN
756: T3 |
0,03-0,15 |
0,800 |
1,40-2,00 |
0,025 |
0,025 |
0,500 |
0,200 |
0,200 |
0,080 |
The mechanical properties are largely determined by the applied
fluxes.
|
||||
|
|
|
|
|
|
|
|
|
|
|
|||||
|
|
0,300 |
|
|
|
|
|
|
|
|
|||||
|
AWS/ASME-A5.17: EC1 |
|
|
|
|
|
|
|
|
|
|||||
DR-FS BPR 01
|
DIN EN
756: T3 |
0,03-0,15 |
0,800 |
1,40-2,00 |
0,025 |
0,025 |
0,500 |
0,200 |
0,200 |
0,080 |
The mechanical properties are largely determined by the applied
fluxes.
|
||||
|
|
|
|
|
|
|
|
|
|
|
|||||
|
|
0,300 |
|
|
|
|
|
|
|
|
|||||
|
AWS/ASME-A5.17: EC1 |
|
|