Part 5 - low-alloy steels, "higher and high-strength steels"
|
Quality |
Standard |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
V |
Re |
Rm |
A |
KV |
at |
|
|
|
Cu |
Al |
Ti+Zr |
|
|
|
|
|
|
MPa |
MPa |
(%) |
(J) |
°C |
|
Wire electrodes for arc welding GMAW |
|||||||||||||||
DR-SG NiMo
|
EN ISO 16834-A: GMn3Ni1Mo |
0,120 |
0,40-0,80 |
1,30-1,90 |
0,015 |
0,018 |
0,80-1,30 |
0,150 |
0,25-0,65 |
0,030 |
>690 |
>750 |
>
17 |
>
40 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
0,120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 90 S-G |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG NiMo K
|
EN ISO 16834-A: GMn3Ni1CrMo |
0,100 |
0,50-0,70 |
1,55-1,80 |
0,015 |
0,018 |
1,35-1,60 |
0,20-0,40 |
0,20-0,30 |
0,05-0,13 |
>720 |
>780 |
>
17 |
>
32 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,350 |
0,120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 100 S-G |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG NiMoCr
|
EN ISO 16834-A: GMn3Ni1CrMo |
0,120 |
0,40-0,70 |
1,30-1,80 |
0,015 |
0,018 |
1,20-1,60 |
0,20-0,40 |
0,20-0,30 |
0,05-0,13 |
>720 |
>780 |
>
17 |
>
32 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,350 |
0,120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 100 S-G |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 80 X
|
EN ISO 16834-A: GMn4Ni1,5CrMo |
0,120 |
0,50-0,80 |
1,60-2,10 |
0,015 |
0,018 |
1,30-1,90 |
0,15-0,40 |
0,30-0,65 |
0,030 |
>770 |
>830 |
>
17 |
>
40 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
0,120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 120 S-G |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 100 X/20
|
EN ISO 16834-A: GMn4Ni2CrMo |
0,120 |
0,60-0,90 |
1,60-2,10 |
0,015 |
0,018 |
1,80-2,30 |
0,20-0,45 |
0,45-0,70 |
0,030 |
>890 |
>940 |
>
15 |
>
47 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
0,120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 120 S-G |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 100 X/23
|
EN ISO 16834-A: GMn4Ni2,5CrMo |
0,130 |
0,50-0,80 |
1,60-2,10 |
0,015 |
0,018 |
2,30-2,80 |
0,20-0,60 |
0,30-0,65 |
0,030 |
>930 |
>980 |
>
15 |
>
40 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
0,120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 120 S-G |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Flux cored wires for arc welding GMAW |
|||||||||||||||
DR-F MPR 15
|
EN ISO 18276-A: T69 4 Mn2NiCrMo M M
2 H5 |
0,03-0,10 |
0,900 |
1,40-2,00 |
0,020 |
0,020 |
1,80-2,60 |
0,30-0,60 |
0,30-0,60 |
0,050 |
>690 |
>760 |
>
18 |
>
47 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E110TC-K4MH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F RPR 15
|
EN ISO 18276-A: T69 4 Z P M 1 H5 |
0,03-0,10 |
0,900 |
1,40-2,00 |
0,020 |
0,020 |
1,80-2,60 |
0,30-0,60 |
0,30-0,60 |
0,050 |
>690 |
>760 |
>
17 |
>
47 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E111T1-GMJH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F BPR 15
|
EN ISO 18276-A: T69 5 Mn2NiCrMo B M
4 H5 |
0,03-0,10 |
0,900 |
1,40-2,00 |
0,020 |
0,020 |
1,80-2,60 |
0,30-0,60 |
0,30-0,60 |
0,050 |
>690 |
>760 |
>
17 |
>
47 |
-51 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E110T5-K4MH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F MPR 18
|
EN ISO 18276-A: T55 4 1NiMo M M 2 H5 |
0,03-0,10 |
0,900 |
1,400 |
0,020 |
0,020 |
0,60-1,20 |
0,200 |
0,30-0,60 |
0,050 |
>540 |
>620 |
>
18 |
>
47 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E90C-GMH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Quality |
Standard |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
V |
Re |
Rm |
A |
KV |
at |
|
|
|
Cu |
Al |
Ti+Zr |
|
|
|
|
|
|
MPa |
MPa |
(%) |
(J) |
°C |
|
Flux cored wires for arc welding GMAW |
|||||||||||||||
DR-F RPR 18
|
EN ISO 18276-A: T62 4 1,5NiMo P M 1
H5 |
0,03-0,10 |
0,900 |
1,400 |
0,020 |
0,020 |
1,20-1,80 |
0,200 |
0,30-0,70 |
0,050 |
>620 |
>700 |
>
17 |
>
47 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E91T1-K2MJH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F BPR 18
|
EN ISO 18276-A: T55 4 1NiMo B M 3 H5 |
0,03-0,10 |
0,900 |
1,400 |
0,020 |
0,020 |
0,60-1,20 |
0,200 |
0,30-0,60 |
0,050 |
>550 |
>660 |
>
18 |
>
47 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E90T5-K2GMH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F MPR 20
|
EN ISO 18276-A: T89 4 Mn2NiCrMo M M
2 H5 |
0,03-0,10 |
0,900 |
1,40-2,00 |
0,020 |
0,020 |
1,80-2,60 |
0,30-0,60 |
0,30-0,60 |
0,050 |
>890 |
>980 |
>
15 |
>
47 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E120C-GMH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F BPR 20
|
EN ISO 18276-A: T89 4 Mn2NiCrMo B M
4 H5 |
0,03-0,10 |
0,900 |
1,40-2,00 |
0,020 |
0,020 |
1,80-2,60 |
0,30-0,60 |
0,30-0,60 |
0,050 |
>890 |
>980 |
>
15 |
>
47 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.36: E120T5-GMH4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Welding rods for arc welding TIG |
|||||||||||||||
DR-SG NiMo
|
EN ISO 16834-A: WMn3Ni1Mo T |
0,120 |
0,40-0,80 |
1,30-1,90 |
0,015 |
0,018 |
0,80-1,30 |
0,150 |
0,25-0,65 |
0,030 |
>690 |
>750 |
>
18 |
>
40 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
0,120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 90 S-G |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG NiMo K
|
EN ISO 16834-A: WMn3Ni1CrMo T |
0,100 |
0,50-0,70 |
1,55-1,80 |
0,015 |
0,018 |
1,35-1,60 |
0,20-0,40 |
0,20-0,30 |
0,05-0,13 |
>720 |
>780 |
>
16 |
>
32 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,350 |
0,120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 100 S-G |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG NiMoCr
|
EN ISO 16834-A: WMn3Ni1CrMo T |
0,120 |
0,40-0,70 |
1,30-1,80 |
0,015 |
0,018 |
1,20-1,60 |
0,20-0,40 |
0,20-0,30 |
0,05-0,13 |
>720 |
>780 |
>
16 |
>
32 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,350 |
0,120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 100 S-G |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 80 X
|
EN ISO 16834-A: WMn4Ni1,5CrMo T |
0,120 |
0,50-0,80 |
1,60-2,10 |
0,015 |
0,018 |
1,30-1,90 |
0,15-0,40 |
0,30-0,65 |
0,030 |
>770 |
>830 |
>
16 |
>
40 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
0,120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 120 S-G |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 100 X/20
|
EN ISO 16834-A: WZMn4Ni2CrMo T |
0,120 |
0,60-0,90 |
1,60-2,10 |
0,015 |
0,018 |
1,80-2,30 |
0,20-0,45 |
0,45-0,70 |
0,030 |
>890 |
>940 |
>
17 |
>
47 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
0,120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 120 S-G |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 100 X/23
|
EN ISO 16834-A: WZMn4Ni2,5CrMo T |
0,130 |
0,50-0,80 |
1,60-2,10 |
0,015 |
0,018 |
2,30-2,80 |
0,20-0,60 |
0,30-0,65 |
0,030 |
>930
|
>980 |
> 17 |
> 40 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
0,120 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.28: ER 120 S-G |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Quality |
Standard |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
V |
Re |
Rm |
A |
KV |
at |
|
|
|
Cu |
Al |
Ti+Zr |
|
|
|
|
|
|
MPa |
MPa |
(%) |
(J) |
°C |
|
Wire electrodes for submerged arc welding SAW |
|||||||||||||||
DR-S 3 NiMo 1
|
EN ISO 26304-A: SZ3Ni1Mo (Wire) |
0,07-0,15 |
0,05-0,80 |
1,30-1,90 |
0,020 |
0,020 |
0,80-1,30 |
0,200 |
0,25-0,65 |
|
The mechanical properties are largely determined by the
applied fluxes.
|
||||
|
|
(EN ISO 26304-B: SUGSUN2M2 (Wire)) |
|
|
|
|
|
|
|
|
|
|||||
|
|
|
0,300 |
0,020 |
|
|
|
|
|
|
|
|||||
|
|
AWS/ASME-A5.23: EF 3 |
|
|
|
|
|
|
|
|
|
|||||
DR-S 3 NiMoCr
|
EN ISO 26304-A: SZ3Ni1,5CrMo (Wire) |
0,07-0,14 |
0,05-0,70 |
1,30-1,80 |
0,020 |
0,020 |
1,20-1,70 |
0,15-0,40 |
0,20-0,50 |
|
The mechanical properties are largely determined by the a
pplied fluxes.
|
||||
|
|
(EN ISO 26304-B: SUGSUN2C1M3 (Wire)) |
|
|
|
|
|
|
|
|
|
|||||
|
|
|
0,300 |
0,020 |
|
|
|
|
|
|
|
|||||
|
|
AWS/ASME-A5.23: EM 2 |
|
|
|
|
|
|
|
|
|
|||||
DR-S 3 NiMoCr 2,5
|
EN ISO 26304-A: SZ3Ni2,5CrMo (Wire) |
0,07-0,15 |
0,10-0,25 |
1,20-1,80 |
0,020 |
0,020 |
2,00-2,60 |
0,30-0,85 |
0,40-0,70 |
|
The mechanical properties are largely determined by the
applied fluxes.
|
||||
|
|
(EN ISO 26304-B: SUGSUN4C1M3 (Wire)) |
|
|
|
|
|
|
|
|
|
|||||
|
|
|
0,300 |
0,020 |
|
|
|
|
|
|
|
|||||
|
|
AWS/ASME-A5.23: EM 4 |
|
|
|
|
|
|
|
|
|
|||||
DR-S 100 X
|
EN ISO 26304-A: SZ4Ni2CrMo (Wire) |
0,08-0,12 |
0,30-0,90 |
1,60-2,10 |
0,015 |
0,015 |
1,80-2,60 |
0,20-1,00 |
0,45-0,70 |
|
The mechanical properties are largely determined by the
applied fluxes.
|
||||
|
|
(EN ISO 26304-B: SUGSUN5C2M3 (Wire)) |
|
|
|
|
|
|
|
|
|
|||||
|
|
|
0,300 |
0,020 |
|
|
|
|
|
|
|
|||||
|
|
AWS/ASME-A5.28: ER 120 S-G |
|
|
|
|
|
|
|
|
|
|||||
DR-S 110 X
|
EN ISO 26304-A: SZ3Ni2,5CrMo (Wire) |
0,07-0,15 |
0,10-0,25 |
1,20-1,80 |
0,015 |
0,015 |
2,00-2,60 |
0,30-0,85 |
0,40-0,70 |
|
The mechanical properties are largely determined by the
applied fluxes.
|
||||
|
|
(EN ISO 26304-B: SUGSUN5C2M3 (Wire)) |
|
|
|
|
|
|
|
|
|
|||||
|
|
|
0,300 |
0,020 |
|
|
|
|
|
|
|
|||||
|
|
AWS/ASME-A5.28: ER 120 S-G |
|
|
|
|
|
|
|
|
|
|||||
|
Quality |
Standard |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
V |
Re |
Rm |
A |
KV |
at |
|
|
|
Cu |
Al |
Ti+Zr |
|
|
|
|
|
|
MPa |
MPa |
(%) |
(J) |
°C |
|
Covered electrodes for electric hand-welding NMA |
|||||||||||||||
DR-E NiMn B
|
EN ISO 2560-A: E46 6 1Ni B 4 2 H5 |
|
|
1,400 |
|
|
0,60-1,20 |
0,200 |
0,200 |
0,050 |
>520 |
>600 |
>
25 |
>120 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.5: E8018-C3 H 4 R |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-E NiMo B
|
DIN EN
757: E62 4 Mn1NiMo B 4 2 H5 |
0,030 |
|
1,40-2,00 |
0,025 |
0,020 |
0,60-1,20 |
0,200 |
0,30-0,60 |
0,050 |
>620 |
>640 |
>
20 |
>
60 |
-40 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.5: E9018-G / E10018-G |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-E NiMoCr B
|
DIN EN
757: E62 6 Mn2NiCrMo B T 4 2 H5 |
0,03-0,10 |
|
1,40-2,00 |
0,025 |
0,020 |
1,80-2,60 |
0,30-0,60 |
0,30-0,60 |
0,050 |
>700 |
>750 |
>
22 |
>
47 |
-60 °C |
|
|
|
|
|
|
|
|
|
|
|
||||||