Part 6 - stainless steel, ferritic, martensitic, martensitic, austenitic-ferritic
(Duplex, Superduplex) and austenitic steels
|
Quality |
Standard |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
V |
Re |
Rm |
A |
KV |
at |
|
|
|
Cu |
Al |
Ti+Zr |
|
|
|
|
|
|
MPa |
MPa |
(%) |
(J) |
°C |
|
Wire electrodes for arc welding GMAW |
|||||||||||||||
DR-SG 4316
|
EN ISO 14343-A: G 19 9 L Si |
0,030 |
0,65-1,20 |
1,00-2,50 |
0,030 |
0,020 |
9,00-11,00 |
19,00-21,00 |
0,500 |
|
>320
|
>510 |
> 25 |
> 32 |
20 °C |
|
|
(EN ISO 14343-B: 308LSi) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4316 |
0,500 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 308 L Si |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 4332
|
EN ISO 14343-A: G 23 12 L Si |
0,030 |
0,65-1,20 |
1,00-2,50 |
0,030 |
0,020 |
11,00-14,00 |
0,06-0,12 |
0,500 |
|
>320
|
>510 |
> 25 |
>115 |
20 °C |
|
|
(EN ISO 14343-B: 309LSi) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4322 |
0,500 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 309 L Si |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 4337
|
EN ISO 14343-A: G 29 9 |
0,150 |
1,000 |
1,00-2,50 |
0,030 |
0,020 |
8,00-12,00 |
28,00-32,00 |
0,500 |
|
>450
|
>650 |
> 15 |
>100 |
20 °C |
|
|
(EN ISO 14343-B: 312) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4337 |
0,500 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 312 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 4351
|
EN ISO 14343-A: G 13 4 |
0,050 |
1,000 |
1,000 |
0,030 |
0,020 |
3,00-5,00 |
11,00-14,00 |
0,40-1,00 |
|
>500
|
>750 |
> 15 |
> 50 |
20 °C |
|
|
(EN ISO 14343-B: 410NiMo) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4351 |
0,500 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 410 NiMo |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 4370
|
EN ISO 14343-A: G 18 8 Mn |
0,200 |
1,200 |
5,00-8,00 |
0,030 |
0,030 |
7,00-10,00 |
17,00-20,00 |
0,500 |
|
>350
|
>500 |
> 25 |
>140 |
20 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4370 |
0,500 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 307 L |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 4430
|
EN ISO 14343-A: G 19 12 3 L Si |
0,030 |
0,650 |
1,00-2,50 |
0,030 |
0,020 |
11,00-14,00 |
18,00-20,00 |
2,50-3,00 |
|
>320
|
>510 |
> 25 |
>130 |
20 °C |
|
|
(EN ISO 14343-B: 316LSi) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4430 |
0,500 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 316 L Si |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 4453
|
EN ISO 14343-A: G Z 18 16 5 N L |
0,030 |
1,000 |
1,00-4,00 |
0,030 |
0,020 |
16,00-19,00 |
17,00-20,00 |
3,50-5,00 |
|
>300
|
>480 |
> 25 |
>110 |
20 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4453 |
0,500 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 317 LN (mod.) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 4455 |
EN ISO 14343-A: G 20 16 3 Mn N L |
0,030 |
1,000 |
5,00-9,00 |
0,030 |
0,020 |
18,00-18,00 |
|
2,50-4,50 |
|
>320
|
>510 |
> 25 |
|
|
|
|
EN ISO 14343-B: 316LMn |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4455 |
0,500 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 316L (mod.) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 4462
|
EN ISO 14343-A: G 22 9 3 N L |
0,030 |
1,000 |
2,500 |
0,030 |
0,020 |
7,00-10,00 |
21,00-24,00 |
2,50-4,00 |
|
>450
|
>550 |
> 20 |
>160 |
20 °C |
|
|
(EN ISO 14343-B: 2209) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4462 |
0,500 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 2209 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG
4501
|
EN ISO 14343-A: G 25 9 4 N L |
0,030 |
1,000 |
2,500 |
0,030 |
0,020 |
8,00-10,50 |
24,00-27,00 |
2,50-4,50 |
|
>550
|
>620 |
> 18 |
> 80 |
20 °C |
|
|
(EN ISO 14343-B: 2594) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
1,500 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 2594 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 4502
|
EN ISO 14343-A: G 17 |
0,120 |
1,000 |
1,000 |
0,030 |
0,020 |
0,500 |
16,00-19,00 |
0,500 |
|
>300 |
>450 |
>
15 |
350-400 |
HB 1. Lay |
|
|
(EN ISO 14343-B: 430) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4502 |
0,500 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 430 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Quality |
Standard |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
V |
Re |
Rm |
A |
KV |
at |
|
|
|
Cu |
Al |
Ti+Zr |
|
|
|
|
|
|
MPa |
MPa |
(%) |
(J) |
°C |
|
Wire electrodes for arc welding GMAW |
|||||||||||||||
DR-SG 4511
|
EN ISO 14343-A: G 18 L Nb |
0,020 |
0,500 | 0,800 |
0,030 |
0,020 |
0,300 | 17,80-18,80 | 0,300 |
|
>220 |
>410 |
>
15 |
||
|
|
(EN ISO 14343-B: 430LNb) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4511 |
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 430LNb |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 4519
|
EN ISO 14343-A: G 20 25 5 Cu L |
0,030 |
1,000 |
1,00-4,00 |
0,030 |
0,020 |
24,00-27,00 |
19,00-22,00 |
4,00-6,00 |
|
>320 |
>510 |
>
25 |
>120 |
20 °C |
|
|
(EN ISO 14343-B: 385) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4519 |
1,00-2,00 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 385 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 4551
|
EN ISO 14343-A: G 19 9 Nb Si |
0,080 |
0,65-1,20 |
1,00-2,50 |
0,030 |
0,020 |
9,00-11,00 |
19,00-21,00 |
0,500 |
|
>350 |
>550 |
>
25 |
>
65 |
20 °C |
|
|
(EN ISO 14343-B: 347Si) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4551 |
0,500 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 347 Si |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 4563
|
EN ISO 14343-A: G 27 31 4 Cu L |
0,030 |
1,000 |
1,00-3,00 |
0,030 |
0,020 |
30,00-33,00 |
26,00-29,00 |
3,00-4,50 |
|
>240 |
>500 |
>
25 |
>
75 |
20 °C |
|
|
(EN ISO 14343-B: 383) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4563 |
0,70-1,50 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 383 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-SG 4576
|
EN ISO 14343-A: G 19 12 3 Nb Si |
0,080 |
0,65-1,20 |
1,00-2,50 |
0,030 |
0,020 |
11,00-14,00 |
18,00-20,00 |
2,50-3,00 |
|
>350 |
>550 |
>
25 |
>
65 |
20 °C |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4576 |
0,500 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.9: ER 318 Si |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Quality |
Standard |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
V |
Re |
Rm |
A |
KV |
at |
|
|
|
Cu |
Al |
Ti+Zr |
|
|
|
|
|
|
MPa |
MPa |
(%) |
(J) |
°C |
|
Flux cored wires for arc welding GMAW |
|||||||||||||||
DR-F 4316 M
|
EN ISO 17633-A: T 19 9 L M M 1 |
0,040 |
1,200 |
2,000 |
0,030 |
0,025 |
9,00-11,00 |
18,00-21,00 |
0,300 |
|
>320 |
>510 |
>
30 |
>
30 |
-196 °C |
|
|
(EN ISO 17633-B: TS308L-FM1) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4316 |
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.22: EC 308L |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F 4316 R
|
EN ISO 17633-A: T 19 9 L R M 3
(C3) |
0,040 |
1,200 |
2,000 |
0,030 |
0,025 |
9,00-11,00 |
18,00-21,00 |
0,300 |
|
>320 |
>510 |
>
30 |
>
30 |
-196 °C |
|
|
(EN ISO 17633-B: TS308L-FM0) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4316 |
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.22: E 308LT0-1/T0-4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F 4316 RS
|
EN ISO 17633-A: T 19 9 L P M 1
(C1) |
0,040 |
1,200 |
2,000 |
0,030 |
0,025 |
9,00-11,00 |
18,00-21,00 |
0,300 |
|
>320 |
>510 |
>
30 |
>
30 |
-196 °C |
|
|
(EN ISO 17633-B: TS308L-FM1) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4316 |
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.22: E 308LT1-1/1-4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F 4316 B
|
EN ISO 17633-A: T 19 9 L Z M 3 |
0,040 |
1,200 |
2,000 |
0,030 |
0,025 |
9,00-11,00 |
18,00-21,00 |
0,300 |
|
>320 |
>510 |
>
30 |
>
30 |
-196 °C |
|
|
(EN ISO 17633-B: TS308L-FM0) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4316 |
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.22: E 308LT0-4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Quality |
Standard |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
V |
Re |
Rm |
A |
KV |
at |
|
|
|
Cu |
Al |
Ti+Zr |
|
|
|
|
|
|
MPa |
MPa |
(%) |
(J) |
°C |
|
Flux cored wires for arc welding GMAW |
|||||||||||||||
DR-F 4332 M
|
EN ISO 17633-A: T 23 12 L M M 1 |
0,040 |
1,200 |
2,500 |
0,030 |
0,025 |
11,00-14,00 |
22,00-25,00 |
0,300 |
|
>320 |
>510 |
>
25 |
>
35 |
-60 °C |
|
|
(EN ISO 17633-B: TS309L-FM1) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4332 |
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.22: EC 309L |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F 4332 R
|
EN ISO 17633-A: T 23 12 L R M 3
(C3) |
0,040 |
1,200 |
2,500 |
0,030 |
0,025 |
11,00-14,00 |
22,00-25,00 |
0,300 |
|
>320 |
>510 |
>
25 |
>
35 |
-60 °C |
|
|
(EN ISO 17633-B: TS309L-FM0) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4332 |
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.22: E 309LT0-1/T0-4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F 4332 RS
|
EN ISO 17633-A: T 23 12 L P M 1
(C1) |
0,040 |
1,200 |
2,500 |
0,030 |
0,025 |
11,00-14,00 |
22,00-25,00 |
0,300 |
|
>320 |
>510 |
>
25 |
>
35 |
-60 °C |
|
|
(EN ISO 17633-B: TS309L-FM1) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4332 |
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.22: E 309LT1-1/T1-4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F 4337 M
|
EN ISO 17633-A: T 29 9 M M 1 |
0,150 |
1,200 |
2,500 |
0,035 |
0,025 |
8,00-12,00 |
27,00-31,00 |
0,300 |
|
>450
|
>650 |
> 15 |
> 40 |
20 °C |
|
|
(EN ISO 17633-B: TS312-FM1) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4337 |
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.22: EC 312 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F 4337 R
|
EN ISO 17633-A: T 29 9 R M 3
(C3) |
0,150 |
1,200 |
2,500 |
0,035 |
0,025 |
8,00-12,00 |
27,00-31,00 |
0,300 |
|
>450
|
>650 |
> 15 |
> 40 |
20 °C |
|
|
(EN ISO 17633-B: TS312-FM0) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4337 |
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.22: E 312T0-1/T0-4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F 4337 RS
|
EN ISO 17633-A: T 29 9 P M 1
(C1) |
0,150 |
1,200 |
2,500 |
0,035 |
0,025 |
8,00-12,00 |
27,00-31,00 |
0,300 |
|
>450
|
>650 |
> 15 |
> 40 |
20 °C |
|
|
(EN ISO 17633-B: TS312-FM1) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4337 |
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.22: E 312T1-1/T1-4 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F 4370 M
|
EN ISO 17633-A: T 18 8 Mn M M 1 |
0,200 |
1,200 |
4,50-7,50 |
0,035 |
0,025 |
7,00-10,00 |
17,00-20,00 |
0,300 |
|
>350
|
>500 |
> 25 |
> 50 |
20 °C |
|
|
(EN ISO 17633-B: TS307-FM1) |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Werkstoff-Nr.: 1.4370 |
0,300 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
AWS/ASME-A5.22: ~EC 307 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
DR-F 4370 R
|
EN ISO 17633-A: T 18 8 Mn R M 3
(C3) |
0,200 |
1,200 |
4,50-7,50 |
0,035 |
0,025 |
| ||||||||